نبذة مختصرة : The investigating results are given for the oxidation kinetics of the composite material on base of both the discontinuous carbon fibers and the phenolformaldehyde resin. According to the results of the thermal analyses amid the oxidation condition the oxidation model was elaborated both for single components and for the composite material in total. The fiber's oxidizing is one-stage, the resin's oxidizing is two-stage, the composite oxidizes in three stages. Based on the calculated parameters of the reaction the isothermal curves were plotted for the temperature within 220‒300 °C at intervals of 10 °C and holding at the heating time up to 5 hours. It was established that at 300 °C during 5 hours the composite material by oxidation lost no more than 5 % of its initial mass. Ill. 3. Ref. 14. Tab. 2. ; Приведены результаты исследования кинетики окисления композиционного материала на основе дискретного углеродного волокна и модифицированной фенолоформальдегидной смолы. По результатам термического анализа в условиях окислительной среды установлена модель окисления как отдельных компонентов, так и композиционного материала в целом. Окисление волокон протекает в одну стадию, смолы ― в две стадии, для композита характерен трехстадийный режим окисления. По рассчитанным параметрам реакции построены изотермы для интервала 220‒300 °C с шагом 10 °C и выдержкой до 5 ч. Установлено, что при 300 °C в течение 5 ч в результате окисления композит теряет не более 5 % исходной массы.
Relation: https://newogneup.elpub.ru/jour/article/view/886/830; Morgan, P. Carbon fiber and their composites / P. Morgan. ― Boca Raton, Florida : Taylor & Francis Group, 2005. ― P. 1011‒1200.; Фиалков, А. С. Углерод, межслоевые соединения и композиты на его основе / А. С. Фиалков. ― М. : Аспект Пресс, 1997. ― 718 с.; Blanco, C. The stabilization of carbon fibers studied by micro-thermal analysis / C. Blanсo, S. Lu, S. Appleyard, B. Rand // Carbon. ― 2003. ― Vol. 41, № 1. ― P. 165‒171.; Boehm, H. Surface oxides on carbon and their analysis: a critical assessment / H. Boehm // Carbon. ― 2002. ― Vol. 40. ― P. 145‒149.; Cho, D. Microstructural evidence for the thermal oxidation protection of carbon/phenolic towpregs and composites / D. Cho, H. Ha, Y. Lim // Carbon. ― 1996. ‒ Vol. 34, № 7. ― P. 163‒190.; Fitzer, E. The future of carbon-carbon composites / E. Fitzer // Carbon. ― 1988. ― Vol. 24, № 2. ― P. 163‒190.; Говоров, А. В. Исследование кинетики окисления углеродных волокон различных типов / А. В. Говоров, А. А. Галигузов, Н. А. Тихонов [и др.] // Новые огнеуоры. ― 2015. ― № 11. ― С. 34‒39. Govorov, A. Study of different types of carbon fiber oxidation kinetics / A. Govorov, A. Galiguzov, N. Tikhonov [et al.] // Refractories and Industrial Ceramics. ― 2016. ― Vol. 56, № 6. ― P. 605‒609.; Kimberly, A. Mechanisms of the pyrolysis of phenolic resin in a carbon/phenolic composite / A. Kimberly, T. Saliba // Carbon. ― 1995. ― Vol. 33, № 11. ― P. 1509‒1515.; Wong, H. Measurement of pyrolysis products from phenolic polymer thermal decomposition / H. Wong, J. Peck, R. Edwarts [et al.] // AIAA SciTech. ― 2014.; ASTM D4102-82(2015). Standard test method for thermal oxidative resistance of carbon fibers, ASTM International : West Conshohocken, PA, 2015 (www. astm.org).; Friedman, H. Kinetics of thermal degradation of charforming plastics from thermogravimetry. Application to a phenolic plastic / H. Friedman // J. Polym. Sci. : Polymer Symposia.― 1964. ― Vol. 6, № 1. ― P. 183‒195.; Ozawa, T. A new method of analyzing termogravimetric data / T. Ozawa // Bull. Chem. Soc. ― 1965. ― Vol. 38, № 11. ― P. 1881‒1886.; Opfermann, J. Kinetic analysis using multivariate non-linear regression / J. Opfermann // J. Therm. Anal. Calorium. ― 2000. ― Vol. 60. ― P. 641‒658.; Guo, W. Kinetics and mechanisms of non-isothermal oxidation of graphite in air / W. Guo, H. Xiao, G. Zhang // Corros. Sci. ― 2008. ― Vol. 50. ― P. 2007‒2011; https://newogneup.elpub.ru/jour/article/view/886
Rights: Authors who publish with this journal agree to the following terms:Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access). ; Авторы, публикующие в данном журнале, соглашаются со следующим:Авторы сохраняют за собой авторские права на работу и предоставляют журналу право первой публикации работы на условиях лицензии Creative Commons Attribution License, которая позволяет другим распространять данную работу с обязательным сохранением ссылок на авторов оригинальной работы и оригинальную публикацию в этом журнале.Авторы сохраняют право заключать отдельные контрактные договорённости, касающиеся не-эксклюзивного распространения версии работы в опубликованном здесь виде (например, размещение ее в институтском хранилище, публикацию в книге), со ссылкой на ее оригинальную публикацию в этом журнале.Авторы имеют право размещать их работу в сети Интернет (например в институтском хранилище или персональном сайте) до и во время процесса рассмотрения ее данным журналом, так как это может привести к продуктивному обсуждению и большему количеству ссылок на данную работу (См. The Effect of Open Access).
Processing Request
No Comments.