نبذة مختصرة : The TC4 alloy is widely used in aerospace and marine engineering due to its excellent mechanical properties and corrosion resistance. However, titanium alloys often face fretting wear problems during use, which affect their long-term stability and service life. This study investigates the effects of surface mechanical attrition treatment (SMAT) time on the surface morphology, microstructure, stress distribution, and fretting wear properties of TC4 alloy. Characterization was performed using white light interferometry, EBSD, SEM, XRD, and microhardness measurements. The results show that SMAT significantly changes the surface and wear properties of TC4 alloy. With the increase in SMAT time from 0 to 240 min, the surface roughness (Ra), hardness, deformation depth, and stress gradually increase while the grain size decreases. After 240 min of SMAT, the TC4 alloy exhibited optimal fretting wear resistance, achieving a wear depth of 14.27 μm, a wear volume of 2.48 × 106 μm3, and a wear rate of 1.24 × 103 μm3/s. This represents a significant improvement, corresponding to an approximate 32.8% reduction in wear depth and a ~48% reduction in both wear volume and wear rate compared to the untreated sample.
Processing Request
No Comments.