نبذة مختصرة : The content of this article aims to determine the value of the best crystal formation by hot crystallization using Response Surface Methodology with the Composite Central Design (CCD) method, then the crystals are identified using XRF (X-Ray Fluorescence) analysis. The hot crystallization method at a temperature of 90°C with a stirring speed of 500 rpm was used with variations in reaction time and sulfuric acid concentration. The reaction times used were 50, 55, 60, 65, and 70 minutes, and the sulfuric acid concentrations were 10%, 12%, 14%, 16%, and 18%. The highest mass of copper sulfate crystals obtained was 5.3908 grams with a reaction time of 70 minutes and a sulfuric acid concentration of 18%, with the highest chemical element in the crystal being Cu at 76.06%. ; Pembuatan tembaga sulfat dengan proses kristalisasi memiliki dua cara yaitu kristalisasi dingin dan kristalisasi panas. Proses kristalisasi dingin memerlukan waktu yang cukup lama dibandingkan dengan kristalisasi panas untuk menghasilkan kristal tembaga sulfat. Penelitian ini bertujuan untuk mengetahui nilai pembentukan kristal terbaik dengan kristalisasi panas menggunakan Response Surface Methodology (RSM) dengan metode Composite Central Design (CCD) kemudian kristal diidentifikasi menggunakan analisa X-Ray Fluorescence (XRF). Metode kristalisasi panas pada suhu 90°C dengan kecepatan pengadukan 500rpm menggunakan variasi waktu reaksi dan konsentrasi asam sulfat. waktu reaksi yang digunakan yaitu 50, 55, 60, 65, dan 70 menit dan konsentrasi asam sulfat sebesar 10%, 12%, 14%, 16%, dan 18%. Massa kristal tembaga sulfat terbanyak didapatkan sebesar 5,3908gram pada variasi waktu reaksi 70 menit dan konsentrasi asam sulfat 18% dengan unsur kimia terbanyak dalam kristal yaitu Cu sebesar 76,06%.
Processing Request
No Comments.