نبذة مختصرة : Based on the analysis of the technological principles of managing the formation of nonmetallic inclusions and the results of additional studies, optimal process conditions for out-of-furnace processing of steel were established, ensuring not only low contamination of nonmetallic inclusions (HB), but also the formation of nonmetallic inclusions of a favorable morphology that do not adversely affect the corrosion resistance of steel. It is shown that this is achieved by regulated input of aluminum for deoxidation and alloying of steel, limiting its content in steel, limiting the input temperature of aluminum and calcium at the final processing stage, as well as the duration of the flushing period. For steel, micro-alloyed with titanium, it is also possible to form another type of HB, which also do not adversely affect the corrosion resistance of steel. The oxide component of such HB with a high content of calcium and titanium acquires a rounded shape. The formation of such HB is achieved by the regulated input of aluminum, titanium and calcium at the final stage of processing. ; Установлены оптимальные технологические режимы внепечной обработки стали, обеспечивающие не только низкую загрязненность неметаллическими включениями (НВ), но и формирование НВ благоприятной морфологии, не оказывающих отрицательного влияния на коррозионную стойкость стали. Показано, что это достигается регламентированным вводом Al на этапах раскисления и легирования стали, ограничением температуры ввода Al и Ca на заключительной стадии обработки, а также продолжительности промывочного периода. Для микролегированной Ti стали возможно формирование другого типа НВ, не оказывающих отрицательного влияния на коррозионную стойкость стали. Оксидная составляющая таких НВ с повышенным содержанием Ca и Ti приобретает округлую форму. Формирование таких НВ достигается регламентированным вводом Al, Ti и Ca на завершающей стадии обработки.
Relation: https://newogneup.elpub.ru/jour/article/view/1296/1122; Родионова, И. Г. Современные подходы к повыше нию коррозионной стойкости и эксплуатационной надежности сталей для нефтепромысловых трубопро водов / И. Г. Родионова, А. И. Зайцев, О. Н. Бакланова [и др.]. ― М. : Металлургиздат, 2012. ― 172 с.; Амежнов, А. В. Особенности и механизмы корро зионного разрушения сталей в различных условиях эксплуатации нефтепромысловых трубопроводов / А. В. Амежнов // Проблемы черной металлургии и мате риаловедения. ― 2019. ― № 2. ― С. 34‒42.; Зайцев, А. И. Природа и механизмы образования в стали коррозионно-активных неметаллических включений. Пути обеспечения чистоты стали по этим включениям. Коррозионно-активные неметаллические включения в углеродистых и низколегированных сталях : cб. трудов / А. И. Зайцев, И. Г. Родионова, С. Д. Зинченко [и др.]. ― М. : Металлургиздат, 2005. ― C. 37‒51.; Родионова, И. Г. Новые подходы к повышению эксплуатационной надежности сталей для нефтепромысловых трубопроводов и возможности их обеспечения при современном уровне развития металлургических технологий. Коррозионные марки сталей в трубной промышленности : cб. трудов / И. Г. Родионова, А. И. Зайцев, О. Н. Бакланова [и др.]. ― Таганрог, 2009. ― С. 2‒17.; Зайцев, А. И. Комплексные неметаллические включения и свойства стали / А. И. Зайцев, В. С. Крапошин, И. Г. Родионова [и др.]. ― М. : Металлургиздат, 2015. ― 276 с.; Аксельрод, Л. М. Комплексный подход к вопросу повышения стойкости футеровок сталеразливочных ковшей / Л. М. Аксельрод, Е. М. Сладков, С. А. Дзярский // Металл и литье Украины. ― 2012. ― № 10. ― С. 35‒39.; Родионова, И. Г. Влияние неметаллических вклю чений на коррозионную стойкость углеродистых и низколегированных сталей для нефтепромысловых трубопроводов / И. Г. Родионова, О. Н. Бакланова, А. В. Амежнов [и др.] // Сталь. ― 2017. ― № 10. ― С. 41‒48.; Амежнов, А. В. Технологические принципы управления формированием неметаллических вклю чений в углеродистых и низколегированных сталях для повышения их коррозионной стойкости в водных средах / А. В. Амежнов // Новые огнеупоры. ― 2019. ― № 8. ― С. 63‒69.; Jo, S. Thermodynamics on the formation of spinel (MgO·Al2 O3 ) inclusion in liquid iron containing chromium / S. Jo, B. Song, S. Kim // Met. Mater. Trans. B. ― 2002. ― Vol. 33B. ― Р. 703‒709.; Park, J. H. Formation mechanism of spinel-type inclusions in high-alloyed stainless steel melts / J. H. Park // Met. Mater. Trans. B. ― 2007. ― Vol. 38B. ― Р. 657‒663.; Osio, A. S. The effect of solidification on the formation and growth of inclusions in low carbon steel welds / A. S. Osio, S. Liu, D. L. Olson // Material Science Engineering A. ― 1996. ― Vol. 221. ― Р. 122‒133.; Yang, Shufeng. Formation and modification of MgOAl2 O 3 -based inclusions in alloy steels / Shufeng Yang, Qiangqiang Wang, Lifeng Zhang [et al.] // The Minerals, Metals & Materials. Society and ASM International. ― 2012. DOI:10.1007/s11663-012-9663-1.; Амежнов, А. В. Влияние химического состава неметаллических включений на коррозионную стойкость углеродистых и низколегированных сталей в водных средах, характерных для условий эксплуатации нефтепромысловых трубопроводов / А. В. Амежнов, И. Г. Родионова, А. И. Зайцев [и др.] // Проблемы черной металлургии и материаловедения. ― 2018. ― № 3. ― С. 81‒90.; Амежнов, А. В. Влияние химического и фазового состава неметаллических включений на коррозионную стойкость углеродистых и низколегированных сталей в водных средах, характерных для условий эксплуатации нефтепромысловых трубопроводов / А. В. Амежнов, И. Г. Родионова // Металлург. ― 2019. ― № 7. ― С. 45‒52.; Пат. 2554659 Российская Федерация. Способ оценки коррозионной стойкости углеродистых и низколегированных трубных сталей и труб, изготовленных из них / Родионова И. Г., Зайцев А. И., Бакланова О. Н., Казанков А. Ю., Эндель Н. И., Кудашов Д. В., Семернин Г. В., Цибров С. Е. ― № 2014104772/28; заявл. 12.02.14; опубл. 15.06.15, Бюл. № 18.; Казаков, А. А. Исследование литой структуры промышленного сляба ферритно-перлитной стали / А. А. Казаков, О. В. Пахомова, Е. И. Казакова // Черные металлы. ― 2012. ― № 11.― С. 9‒15.; Иоффе, А. В. Влияние модифицирования редко земельными металлами на механические и корро зионные свойства низколегированных сталей / А. В. Иоффе, Т. В. Тетюева, Т. В. Денисова // Вектор науки ТГУ. ― 2010. ― № 14. ― С. 41‒46.; https://newogneup.elpub.ru/jour/article/view/1296
Rights: Authors who publish with this journal agree to the following terms:Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access). ; Авторы, публикующие в данном журнале, соглашаются со следующим:Авторы сохраняют за собой авторские права на работу и предоставляют журналу право первой публикации работы на условиях лицензии Creative Commons Attribution License, которая позволяет другим распространять данную работу с обязательным сохранением ссылок на авторов оригинальной работы и оригинальную публикацию в этом журнале.Авторы сохраняют право заключать отдельные контрактные договорённости, касающиеся не-эксклюзивного распространения версии работы в опубликованном здесь виде (например, размещение ее в институтском хранилище, публикацию в книге), со ссылкой на ее оригинальную публикацию в этом журнале.Авторы имеют право размещать их работу в сети Интернет (например в институтском хранилище или персональном сайте) до и во время процесса рассмотрения ее данным журналом, так как это может привести к продуктивному обсуждению и большему количеству ссылок на данную работу (См. The Effect of Open Access).
Processing Request
No Comments.