Comparison of Cu-CHA-Zeolites in the Hybrid NSR-SCR Catalytic System for NO x Abatement in Mobile Sources.

DeNOx activity in a NSR–SCR hybrid system of two copper-containing chabazite-type zeolitic catalysts was addressed. A Pt-Ba-K/Al2O3 model catalyst was used as the NSR (NOx storage and reduction) catalyst. For the SCR (selective catalytic reduction) system, two Cu-CHA zeolites were synthesized employing a single hydrothermal synthesis method assisted with ultrasound and incorporating Cu in a 2 wt.%, 2Cu-SAPO-34 and 2Cu-SSZ-13. The prepared catalysts were characterized, and the crystallinity, surface area, pore size, HR-TEM and EDX mapping, coordination of Cu ions and acidity were compared. The NH3 storage capacity of the SCR catalysts was 1890 and 837 μ mol   NH 3 · g cat − 1 for 2Cu-SAPO-34 and 2Cu-SSZ-13, respectively. DeNOx activity was evaluated for the single NSR system and the double-bed NSR–SCR by employing alternating lean (3%O2) and rich (1%H2) cycles, maintaining a concentration of 600 ppm NO, 1.5% H2O and 0.3% CO2 between 200 and 350 °C. The addition of the SCR system downstream of the NSR catalyst significantly improved NOx conversion mainly at low temperature, maintaining the selectivity to N2 above 80% and reaching values above 90% at 250 °C when the 2Cu-SSZ-13 catalyst was located. The total reduction in the production of NH3 and ~2% of N2O was observed when comparing the NSR–SCR configuration with the single NSR catalyst. [ABSTRACT FROM AUTHOR]

Copyright of Chemistry (2624-8549) is the property of MDPI and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)