نبذة مختصرة : Cellulose acetate and polyisocyanate copolymer synthesized by mechanical mixing of cellulose acetate, polyisocyanate and fumed silicon dioxide in the presence of nickel chloride was carbonized in silicon dioxide template. Copolymer and silicon dioxide template were formed simultaneously. Composite structure and composition was studied with SEM and EDS. SEM showed that porous carbonaceous nanomaterial was synthesized. Formed carbon is represented by coating on silicon dioxide, layered ribbon-like and fibrous structures in template pores with size from several nm (thickness) to several microns (length). Metallic nickel crystals up to 200 nm in size were fabricated in composite pores from Nickel chloride by reduction of Ni2 with products of pyrolysis of organic compounds. Key words: carbon-silica nanomaterials, polyisocyanate, cellulosr acetate, fumed silica, nickel chloride, carbonization. ; Карбонізацією сополімеру ацетату целюлози з поліізоціанатом в матриці із силіцій діоксиду синтезовано вуглець-кремнеземний наноматеріал, який складається із наночасток SiO2 та вуглецевих наноутворень розміром від декількох нм (товщина) до декількох мкм (довжина). Структуру і склад піровуглецю досліджували методами СЕМ та ЕДРС. В присутності у реакційній суміші нікол хлориду в порах композиту додатково до вуглецевого покриття на частинках SiO2 утворюються шарувато-стрічкові та волокнисті наноструктурі вуглецю розміром до декількох мкм та частинки металевого Ніколу розміром до 200 нм. Ключові слова: вуглець-кремнеземні наноматеріали, поліізоціанат, ацетат целюлози, пірогенній кремнезем, нікол хлорид, карбонізація.
Rights: Full-text files published in Physics and Solid-State Chemistry (http://journals.pu.if.ua/index.php/pcss/issue/archive) are licensed in accordance with CC BY 3.0 Authors who publish with this journal agree to the following terms: Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a CC BY Creative Commons Attribution 3.0 Unported License that allows others to share the work with an acknowledgement of the work's authorship.Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).\This Journal hosted on the OJS platform supports the deposit policy of published materials using the SWORD platform. Address of the access point: journals.pu.if.ua/index.php/pcss/article/viewDeposeted system - Optional; Flexible: The author can choose whether or not to deposit. The specified URL indicates a service document, and the author may choose which specific deposit point to use from that document. Deposit occurs after notifying the author of acceptance. ; Повні тексти статей, опубліковані у журналі Фізика і хімія твердого тіла (http://journals.pu.if.ua/index.php/pcss/issue/archive) ліцензованіт згідно умов ліцензії CC BY 3.0 Автори, які публікуються у цьому журналі, погоджуються з наступними умовами: Автори залишають за собою право на авторство своєї роботи та передають журналу право першої публікації цієї роботи на умовах ліцензії CC BY Creative Commons Attribution 3.0 Unported License, котра дозволяє іншим особам вільно копіювати та розповсюджувати опубліковану роботу з обов'язковим посиланням на авторів оригінальної роботи.Автори мають право укладати самостійні додаткові угоди щодо неексклюзивного розповсюдження роботи у тому вигляді, в якому вона була опублікована цим журналом (наприклад, розміщувати роботу в електронному сховищі установи або публікувати у складі монографії), за умови збереження посилання на першу публікацію роботи у цьому журналі.Політика журналу дозволяє і заохочує розміщення авторами в мережі Інтернет (наприклад, у сховищах установ або на особистих веб-сайтах) рукопису роботи, як до подання цього рукопису до редакції, так і під час його редакційного опрацювання, оскільки це сприяє виникненню продуктивної наукової дискусії та позитивно позначається на оперативності та динаміці цитування опублікованої роботи (див. The Effect of Open Access).Цей журнал, який розміщено на платформі OJS, підтримує політику депонування опублікованих матеріалів за допомогою платформи SWORD. Адреса початкової точки доступу: journals.pu.if.ua/index.php/pcss/article/viewСистема депонування - За вибором; Гнучка: Автор може обирати, депонувати свою роботу чи ні. Вказується адреса URL до документу зі списком служб, з якого автор може обрати окрему точку депонування. Депонування відбувається після повідомлення автору про прийняття його рукопису.
Processing Request
No Comments.