A Study on Ordinary Portland Cement Blended with Rice Husk Ash and Metakaolin

This paper tries to investigate the effect of replacing Ordinary Portland cement (OPC) with Metakaolin (MK) and Rice husk ash (RHA) on the physicomechanical properties such as consistency, setting times, soundness and mortar compressive strength of ternary cement up to 40 % cement replacement. The soundness of the blended cement pastes and compressive strength of the blended mortars were conducted using Le Chatelier apparatus and Tonic Technic compression machine while the initial and final setting times were conducted on the blended cement paste using Vicat apparatus. Nineteen ternary cement mortars were prepared to comprise of OPC, RHA MK at different proportions and tested at 2, 7, 28 and 60 days. Results indicated that as RHA was gradually increased up to 25% at constant MK content, the volume expansion of the ternary cement paste increased gradually. On the other hand, as MK was increased from 5-25% at constant RHA, the volume expansion diminished. The water consistency of ternary cement paste experienced a variation as MK was increased up to 25 wt% at constant RHA up to 10 wt%. However, at 10 wt% constant RHA as MK was increased the water demand gradually increased. Similarly, an increase in RHA at constant MK increased the water demands of the ternary blends. An increase in RHA from 5-25 wt% at 5-25 wt% constant MK resulted in an acceleration in the initial and final setting times of cement blends. These accelerations could be attributed to the pozzolanic activity leading in shorter setting time. Whereas a series of accelerations and retardations of both setting times were experienced as the MK was increased from 5-25 wt% at 5-25 wt% constant RHA. It was observed that increment in the MK or RHA up to 10 wt% at constant RHA/MK up to 10 wt% resulted in improved mortar compressive strength of the ternary blend in comparison with control. This improvement was attributed to the high silica/alumina contribution to the matrix by MK inclusion, the C/S ratio in the cement matrix and RHA pozzolanic reactivity ...