نبذة مختصرة : The low strength caused by the single FCC structure of the CrMnFeCoNi high entropy alloy (HEA) limits its application in the field of coating. Here, we prepared high-entropy alloy coatings of CrMnFeCoNi with different ZrC contents on Q235 steel by a plasma transferred arc process. The effects of ZrC on the microstructure and properties of the CrMnFeCoNi HEA coating were investigated by optical microscopy, scanning electron microscope, and X-ray diffraction and by employing a potensiostat/galvanostat. The results showed that ZrC mainly existed in the coatings as a second phase, having little influence on the main crystal structure and micromorphology of the CrMnFeCoNi HEA coating. The hardness of the CrMnFeCoNi HEA coating increased with the ZrC content. ZrC can effectively improve the corrosion resistance of the CrMnFeCoNi HEA coating. In a 1 mol/L NaCl solution with 4 wt% ZrC, the annual corrosion rate was only 5.997% of that of the HEA coating. Nevertheless, the improvement in the wear resistance of CrMnFeCoNi high-entropy alloy coatings was not apparent with the addition of ZrC. Consequently, the addition of ZrC to the FeCoCrNiMn high-entropy alloy coating holds promise for applications in corrosion resistance, particularly in oceanic environments.
No Comments.