نبذة مختصرة : This paper presents and analyzes the results of different curing methods of the different cement treated bases (CTB). Using 3 different curing methods is emulsion cure, wet burlap and wet geotextile. Results from the temperature monitoring data during the curing process at different depths in the CTB show that at the same depth, the curing by emulsion makes the temperature in the CTB higher than the wet burlap method from 120C to 180C and higher than the wet geotextile method from 100C to 130C. Curing method by emulsion makes the temperature of CTB highest, amplitude of temperature fluctuation in the pavement between day and night is up to 230C. For the other 2 methods, the amplitude of thermal fluctuation is lower, the wet burlap method is only about 50C and the wet geotextile method is about 100C. The results of drilled samples determined compressive strength and split compression at 14 days of the cement treated bases by wet burlap the best results. ; Bài báo này trình bày và phân tích kết quả của các phương pháp (PP) bảo dưỡng lớp cấp phối đá dăm gia cố xi măng (CPĐD GCXM) khác nhau. Sử dụng 3 PP bảo dưỡng khác nhau là màng nhũ tương, phủ bao bố kết hợp tưới nước và phủ vải địa kết hợp tưới nước. Kết quả từ dữ liệu quan trắc nhiệt độ trong suốt quá trình bảo dưỡng tại các chiều sâu khác nhau trong lớp CPĐD GCXM cho thấy, ở cùng độ sâu, bảo dưỡng bằng PP nhũ tương có nhiệt độ cao nhất, cao hơn PP bao bố tưới nước từ 120C đến 180C và vải địa tưới nước từ 100C đến 130C. PP bảo dưỡng bằng nhũ tương có biên độ giao động nhiệt độ trong lớp vật liệu giữa ngày và đêm lên đến 230C, PP bao bố có biên độ rất thấp nhất chỉ khoảng 50C và PP bảo dưỡng vải địa có biên độ khoảng 100C. Kết quả mẫu khoan xác định cường độ nén và ép chẻ ở tuổi 14 ngày của PP bảo dưỡng bằng bao bố tưới ẩm cho kết quả tốt nhất.
Processing Request
No Comments.