نبذة مختصرة : In the present work the study of the structural and magnetic properties of the powder composition of Gd0.257-xTbxFe0.743 with x = 0, 0.1285, 0.257, prepared by Mechanical Alloying (MA) in argon atmosphere during 72 hours using a high energy planetary mill is reported. The structural characterization was performed by means of X-ray diractometry (XRD), for the magnetic characterization Mossbauer spectroscopy was used, the hysteresis cycles of the samples were obtained using the VSM (vibration sample magnetometry) of a PPMS (Physical Property Measurement System). The a-Fe phase is presented for all x by a characteristic peak whose intensity remains slightly constant, however, a decrease in the crystallite size of the a-Fe phase is observed, this result is correlated with an increase of its width when is replaced the Gd by the Tb. The results of the Mossbauer spectra at room temperature indicate that the system exhibits a ferromagnetic behavior for all compositions and the hysteresis cycles show that it exhibits magnetically semi-hard behavior. ; En el presente trabajo se reporta el estudio de las propiedades estructurales y magnéticas de la composición en forma de polvo de Gd0.257-xTbxFe0.743 con x=0, 0.1285, 0.257, preparadas por Aleamiento Mecánico (MA) en atmósfera de argón durante 72 horas mediante un molino planetario de alta energía. La caracterización estructural se realizó por medio de Difractometría de rayos X (XRD), para la caracterización magnética se utilizó la espectroscopía Mossbauer, los ciclos de histéresis de las muestras se obtuvieron utilizando un magnetómetro de muestra vibrante VSM (vibration sample magnetometry) de un sistema PPMS (Physical Property Measurement System). La fase de a-Fe se presenta para todo x mediante un pico característico cuya intensidad permanece ligeramente constante; sin embargo, si se observa una disminución del tamaño de cristalito de la fase a-Fe, resultado que se correlaciona con un aumento de su ancho al sustituir el Gd por el Tb. Los resultados de los espectros ...
Relation: https://revistas.unal.edu.co/index.php/rfc/article/view/61394/60929; Arrabal, R., Matykina, E., Pardo, A., Merino, M.C., Paucar, K., Mohedano, M. & Casajús, P. (2012). Corrosion behaviour of AZ91D and AM50 magnesium alloys with Nd and Gd additions in humid environments. Corrosion Science, 55, 351-362.; Avignant D., Largeau E., Gaumet V., Dugat P. & El-Ghozzi, M. (1998). Recent progress in tetravalent terbium chemistry. Journal of alloys and compounds, 275, 1-5.; Chaudari, P., Cuomo, J. J. & Gambino, R. J. (1973). Amorphous Metallic Films for Magneto-optic Applications. Applied Physics Letters, 22 (7), 337-339.; Lutterotti L. & Scardi P. (1990). J. Appl. Crystallogr. 23, 246-252.; Rojas, Y., Oyola, D., Bustos, H., Pérez, G. & Greneche, J. (2012). Study of the Magnetical and Structural Properties of Powders of Tb0.257-xNdxFe0.743 Mechanically Alloyed. Revista Colombiana de Física, 44 (2), 155-158.; Sallica, E., Peña Rodríguez, V. A., Vásquez Mansilla, M. & Butera, A. (2009). Dependencia de las propiedades magnéticas con el espesor en películas delgadas de FePt. Revista de Investigación de Física, 12 (2), 22-29.; Sánchez Villarejo, N. (2007). Del soporte papel perforado y cinta magnética ral disco 3d holográco anatómico nanotecnológico: nuevos soportes magneto-ópticos y ópticos de almacenamiento masivo de información. Revista Anales de Documentación, 10, 429-450.; Soliman, S. A. & Abu Zied, B. M. (2009). Thermal Genesis, Characterization, And Electrical Conductivity Measurements Of Terbium Oxide Catalyst Obtained From Terbium Acetate. Thermochimica Acta, 49 (1), 84-91.; Teillet , J. & Varret, F. (1976) MOSFIT program, Unpublished. Université du Maine, Le Mans, France.; https://revistas.unal.edu.co/index.php/rfc/article/view/61394
Processing Request
No Comments.