Properties and Fabrication of PA66/Surface-Modified Multi-Walled Nanotubes Composite Fibers by Ball Milling and Melt-Spinning

PA66/surface-modified multi-walled carbon nanotubes (MWNTs) composite fibers with a better dispersion and a stronger interfacial interaction between MWNTs and polyamide 66 (PA66) matrix were fabricated via the method of ball milling and melt-spinning. The effects of unmodified (U-MWNTs), acid-modified (MWNTs-COOH) and sodium dodecyl benzenesulfonate-modified MWNTs (MWNTs-SDBS) on the physical mechanical and thermal properties of PA66 were investigated. The results show that, the surface modified nanotube can provide homogeneous dispersion and there is a strong interfacial bonding between PA66 and MWNTs-COOH. A homogeneous dispersion of MWNTs in PA66 matrices without agglomeration is obtained by a facile ball milling method, which can increase the utilization ratio of MWNTs, reduce the required amount of MWNTs and ultimately improve the mechanical properties at a lower filler loading. The tensile strength of composite fibers reaches a maximum which respectively improved by 27% and 24% than that of PA66 fibers, when the mass fraction of MWNTs-SDBS and MWNTs-COOH is 0.1%. It is helpful for decrease the producing costa of the composite fibers. Moreover, the incorporation of MWNTs into PA66 improves the crystallizing temperature, crystallinity and thermal stability. The research shows that a novel facile method is developed for the fabrication of polymer composite fiber.