An easy one-pot solvothermal synthesis of poorly crystalline solid ReS2/C microspheres

Artículo de publicación ISI ; Dense microspheres consisting of poorly crystalline ReS2 embedded in carbon were synthesized with a high yield via a facile one-pot solvothermal route, by reacting dirhenium decacarbonyl, elemental sulfur and an aromatic solvent (benzene, toluene or p-xylene) for 24 h at 180 C. X-ray diffraction (XRD), scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), energy-dispersive X-ray spectroscopy (EDS), Raman spectroscopy, and Fourier transform infrared spectroscopy (FT-IR) techniques were used to characterize the samples. The resulting microspheres were dense, with average diameters between 0.79 and 1.40 mm, had smooth surfaces and were constructed of ReS2 sheet-like structures with 4.5e9.8 wt % of structural amorphous carbon, which is retained as a textural stabilizer after calcination at 800 C. The synthesis was repeated using isopropanol and cyclohexane, whose products were agglomerated grains and botryoidal quasi-spherical particles, respectively. A possible formation mechanism of ReS2/C microspheres was preliminarily presented, in order to clarify the mechanistic differences between the rhenium carbonyl and other transition metal carbonyls used in similar syntheses. ; CONICYT (FONDECYT Grant 1131112), Nucleo Milenio de Magnetismo, CEDENNA, CONACYT (174689), PAPIIT (IN104714-3) and CONICYT doctoral fellowship for the financial supports.