نبذة مختصرة : This work describes the scandium doping effect on the structural and magnetic properties of delafossite-type oxides CuCr1−x Sc x O2. The lattice parameters were found to vary according to Vegard's low. A reflection broadening is observed that is ascribed to local lattice distortion due to the ionic radius difference between Fe3+ and Sc3+. Magnetic susceptibility measurements show that the dominant interactions are antiferromagnetic (AFM) but that doping induces significant changes. A rather monotonous T N2 decrease as x increases, from T N2 = 9.1 K down to T N2 = 5.9 K for x = 0.00 to 0.25, respectively, but T N1 remains almost unchanged. The Sc substitution (S = 0) at the Fe sites (S = 5/2) tend to suppress the low ferromagnetic interactions in the magnetic structure; however, the magnetic exchange coupling J BB decreases under 5.0 meV with increasing x. The electric polarization decreases with x up to 63 μC/m2 for 5 %-Sc to 22 μC/m2 for 25 %-Sc. ... : يصف هذا العمل تأثير منشطات سكانديوم على الخصائص الهيكلية والمغناطيسية لأكاسيد من نوع ديلافوسيت CuCr1 -x Sc x O2. وجد أن المعلمات الشبكية تختلف وفقًا لانخفاض فيجارد. لوحظ اتساع الانعكاس الذي يعزى إلى تشوه شعري موضعي بسبب اختلاف نصف القطر الأيوني بين Fe3 + و Sc3+. تُظهر قياسات الحساسية المغناطيسية أن التفاعلات السائدة هي مضادة للمغناطيسية (AFM) ولكن هذا المنشطات يؤدي إلى تغييرات كبيرة. ينخفض T N2 الرتيب إلى حد ما مع زيادة x، من T N2 = 9.1 كلفن إلى T N2 = 5.9 كلفن لـ x = 0.00 إلى 0.25، على التوالي، لكن T N1 يبقى دون تغيير تقريبًا. يميل استبدال SC (S = 0) في مواقع الحديد (S = 5/2) إلى قمع التفاعلات المغناطيسية الحديدية المنخفضة في البنية المغناطيسية ؛ ومع ذلك، فإن اقتران التبادل المغناطيسي J BB ينخفض إلى أقل من 5.0 ميجا فولت مع زيادة x. ينخفض الاستقطاب الكهربائي مع × تصل إلى 63 ميكرومتر/م 2 لمدة 5 ٪ - SC إلى 22 ميكرومتر/م 2 لمدة 25 ٪ - SC. ...
Processing Request
No Comments.