نبذة مختصرة : International audience ; During additive manufacturing of alloys, just after local heat-matter interactions, a molten material undergoes rapid solidification. Then, for the rest of the building time, it is subjected to cooling/heating cycles in the solid-state i.e., solid-state thermal cycling. The thermo-mechanical forces generated during solid-state thermal cycling can trigger a plethora of micro-mechanisms that can bring about significant microstructural changes that determine the eventual mechanical properties of as-built parts. In this work, the aim is to gain insight on solid-state thermal cyclingdriven evolution of submicron-sized precipitates in an austenitic stainless steel using transmission electron microscopy. To that end, thin-film lamellae are extracted from a pre-built sample and subjected to different in-situ solid-state thermal cycles inside a transmission electron microscope. The solid-state thermal cycles are designed to understand the role of temperature amplitude and rates, number and type of thermal cycles, and post-process annealing on precipitate evolution. High angle annular dark field imaging and energy dispersive X-ray spectroscopy before and after each thermal cycle provide a deep insight on the contribution of different thermal cycling factors on the evolution of precipitate composition, size and morphology. Common trends include diffusion of Mn and Si from Mn-Si-rich oxides into the surrounding matrix, formation of Cr rings around oxide precipitates and S redistribution in non-oxide precipitates. Similar Cr rings and S distributions were also found in precipitates in as-built samples studied in (Upadhyay et al., Sci. Rep. 11 (2021) 10393), which strongly supports the representativeness of these results with respect to what occurs during additive manufacturing.
Processing Request
No Comments.