Thermal and Dielectric Behaviour of Polymer-Based Nanocomposites Flexible Sheets as Highly Stable Dielectric Materials

The silica zinc oxide nanoparticles filled poly-vinylidene-fluoride (PVDF)-based nanocomposite flexible sheets (NC FSs) are synthesized by co-precipitation method. The X-ray diffraction patterns reveal the development of various diffraction planes related to zinc oxide (ZnO) and SiO2 phases. The crystallinity of ZnO phase is decreased with increasing weight percent (wt.%) of silica nanofillers (NFs). The scanning electron microscope microstructure of synthesized PVDF-based NCs FSs is changed with increasing wt.% of silica NFs. The energy-dispersive X-ray spectroscopy and Fourier-transform infrared spectroscopy analyses confirm the presence of different elements and the formation of chemical bonding between them. In high temperature region, the weight-loss of synthesized PVDF-based NCs FSs is decreased from 89.90% to 49.26% with increasing wt.% of silica NFs. The values of dielectric permittivity, loss-factor, impedance, and AC-conductivity of PVDF-based NC FSs synthesized for maximum amount of silica NFs are found to be 13.7, 0.03, 0.16 MΩ, and 19.9×10−6 S/m, respectively. Results show that the synthesized PVDF-based NC FSs are the potential candidates of light emitting diodes and energy storage devices.