نبذة مختصرة : The study aimed to synthesize the adsorbent consisting of activated carbon derived from coffee spent and sodium alginate (AC@AL). The adsorption capacity of Congo red in water was assessed by factors: pH, time, concentration, and mass. The results of thermogravimetric analysis (TGA), and Fourier transform infrared spectroscopy (FT-IR) showed that AC@AL beads were successfully synthesized. Images of scanning electron microscopy (SEM) showed that AC@AL beads had an average diameter of 0.18±0.12 mm, a rough surface with many grooves and pores. The specific surface area (BET) of AC@AL was 251.493 m2/g and the pore diameter was mesopore with a value of 97.26 Å. AC@AL beads adsorbed Congo red in water with a yield of 90.6±0.85% at optimal conditions of pH 2, adsorption time of 2h, and initial concentration of 20ppm. The Congo red adsorption process using AC@AL followed the Freundlich adsorption isotherm model, pseudo-second-order kinetic models, and was a physical adsorption process. ; Nghiên cứu này thực hiện với mục tiêu tổng hợp vật liệu hấp phụ dạng hạt gồm than hoạt tính điều chế từ bã cà phê và alginate (AC@AL). Khả năng hấp phụ Congo red trong nước được đánh giá bởi các yếu tố: pH, thời gian, nồng độ, khối lượng. Các đặc tính của vật liệu được xác định bằng phương pháp phân tích nhiệt trọng lượng (TGA) và phổ hồng ngoại biến đổi Fourier (FT-IR) cho thấy AC@AL đã được tổng hợp thành công. Ảnh hiển vi điện tử quét (SEM) cho thấy, hạt AC@AL có đường kính trung bình 0,18±0,12 mm, bề mặt gồ ghề, có nhiều khe rãnh, lỗ xốp. Diện tích bề mặt riêng (BET) của hạt AC@AL là 251,439 m2/g và đường kính lỗ xốp 97,26 Å thuộc dạng mesoporous. Hạt AC@AL hấp phụ Congo red trong nước với hiệu suất 90,6±0,85% ở điều kiện tối ưu pH 2, thời gian 2 h và nồng độ đầu 20 ppm. Quá trình hấp phụ Congo red trên AC@AL tuân theo mô hình đẳng nhiệt hấp phụ Freundlich, động học hấp phụ giả định bậc 2 và là hấp phụ vật lý.
Processing Request
No Comments.