Evidence for the formation of two types of oxygen interstitials in neutron-irradiated α-Al2O3 single crystals

Authors are indebted to R. Vila for stimulating discussions. Tis work has been carried out within the framework of the EUROfusion Consortium and has received funding from the Euratom research and training programme 2014–2018 and 2019–2020 under Grant agreement No 633053. The views and opinions expressed herein do not necessarily refect those of the European Commission. In addition, the research leading to these results has received funding from the Latvian grant LZP-2018/1-0147 (EV). Institute of Solid State Physics, University of Latvia as the Center of Excellence is supported through the Framework Program for European universities Union Horizon 2020, H2020-WIDESPREAD-01–2016–2017-TeamingPhase2 under Grant Agreement No. 739508, CAMART2 project.
Due to unique optical/mechanical properties and significant resistance to harsh radiation environments, corundum (α-Al2O3) is considered as a promising candidate material for windows and diagnostics in forthcoming fusion reactors. However, its properties are affected by radiation-induced (predominantly, by fast neutrons) structural defects. In this paper, we analyze thermal stability and recombination kinetics of primary Frenkel defects in anion sublattice − the F-type electronic centers and complementary oxygen interstitials in fast-neutron-irradiated corundum single crystals. Combining precisely measured thermal annealing kinetics for four types of primary radiation defects (neutral and charged Frenkel pairs) and the advanced model of chemical reactions, we have demonstrated for the first time a co-existence of the two types of interstitial defects – neutral O atoms and negatively charged O- ions (with attributed optical absorption bands peaked at energies of 6.5 eV and 5.6 eV, respectively). From detailed analysis of interrelated kinetics of four oxygen-related defects, we extracted their diffusion parameters (interstitials serve as mobile recombination partners) required for the future prediction of secondary defect-induced reactions and, eventually, material radiation tolerance.--//-- The article Lushchik, A., Kuzovkov, V.N., Kotomin, E.A. et al. Evidence for the formation of two types of oxygen interstitials in neutron-irradiated α-Al2O3 single crystals. Sci Rep 11, 20909 (2021). https://doi.org/10.1038/s41598-021-00336-0 published under CC BY 4.0 licence.
EURATOM 633053, LZP-2018/1-0147; Institute of Solid State Physics, University of Latvia as the Center of Excellence is supported through the Framework Program for European universities Union Horizon 2020, H2020-WIDESPREAD-01–2016–2017-TeamingPhase2 under Grant Agreement No. 739508, CAMART2 project.