Structure Mediation and Properties of Poly(l-lactide)/Poly(d-lactide) Blend Fibers

Poly(l-lactic acid) (PLLA) and poly(d-lactic acid) (PDLA) blend as-spun fibers (50/50, wt.%) were prepared by melt spinning. Structure mediation under temperature and stress and properties of poly(l-lactic acid)/poly(d-lactic acid)(PLLA/PDLA) as-spun fibers were investigated by wide-angle X-ray scattering (WAXS) and differential scanning calorimetry (DSC). The results show that highly oriented stereocomplex (SC) crystals can be formed in PLLA/PDLA blend fibers drawn at 60 °
C and annealed at 200 °
C. However, at drawn temperature of 80 °
C, only lower oriented SC crystals can be formed. For PLLA/PDLA blend fibers drawn twice at 60 °
C (PLLA/PDLA-60-2), the crystallinity of SC crystals increases with annealing temperature in the range of 200 to 215 °
C, while the degree of orientation decreases slightly. When the annealing temperature is 210 °
C, the crystallinity and orientation of SC crystals in PLLA/PDLA-60-2 fibers reach 51% and &minus
0.39, respectively. Moreover, PLLA/PDLA-60-2-210 fibers exhibit excellent heat-resistant property even at 200 °
C. The results indicate that the oriented PLLA/PDLA blend fibers with high SC crystals content can be regulated in a short time.