نبذة مختصرة : The development of crystalline aluminate-bearing hydrates in portland cement mortars during water storage at room temperature for periods of up to 1 year after an initial heat cure for 12 h has been observed by quantitative X-ray diffraction analysis and backscattered electron imaging. Ettringite was present in the mortars immediately after a short-term cure at 20° and 60°C, calcium carboaluminate (C4ACH11) at 60°C, monosulfate at 85°C, and hydrogarnet at 85°C and above. Ettringite started to form after an induction period ranging from several days to several months after the initial heat cure at 85/100°C, and developed substantially during the period of expansion of the mortar associated with delayed ettringite formation (DEF). Ettringite growth was also observed in the nonexpansive cement mortars. Development of the ettringite bands occurred exclusively in the expansive mortars. Although monosulfate observed in the mortars that had been heat cured at 85°C sometimes increased in amount on initial storage at room temperature, it appeared to vary little in amount for up to 1 year. The amount of hydrogarnet in the heat-cured cement product did not change significantly during storage at room temperature for more than 1 year. DEF expansion of the heat-cured mortars was attributed to ettringite band formation, which started to form at the surface of the cement product and gradually developed inwards.
Processing Request
No Comments.