Study of Poly(3-hydroxybutyrate- co-3-hydroxyvalerate) (PHBV)/Bamboo Pulp Fiber Composites: Effects of Nucleation Agent and Compatibilizer.

In this study, poly(3-hydroxybutyrate- co-3-hydroxyvalerate) (PHBV)/bamboo pulp fiber (BPF) composites were prepared by melt compounding and injection molding. The crystallization ability, tensile strength and modulus, flexural strength and modulus, and impact strength were found substantially increased by the addition of BPF. Tensile and flexural elongations were also moderately increased at low fiber contents (<20%). BPF demonstrated not only higher strength and modulus, but also higher failure strain than the PHBV8 matrix. Boron nitride (BN) was also investigated as a nucleation agent for PHBV8 and maleic anhydride grafted PHBV8 (MA-PHBV8) as a compatibilizer for the composite system. BN was found to increase the overall properties of the neat polymer and the composites due to refined crystalline structures. MA-PHBV8 improved polymer/fiber interactions and therefore resulted in increased strength and modulus. However, the toughness of the composites was substantially reduced due to the hindrance to fiber pullout, a major energy dissipation source during the composite deformation. [ABSTRACT FROM AUTHOR]

Copyright of Journal of Polymers & the Environment is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)