Production of Cu/Diamond Composite Coatings and Their Selected Properties.

This article presents Cu/diamond composite coatings produced by electrochemical reduction on steel substrates and a comparison of these coatings with a copper coating without diamond nanoparticles (<10 nm). Deposition was carried out using multicomponent electrolyte solutions at a current density of 3 A/dm² and magnetic stirring speed of 100 rpm. Composite coatings were deposited from baths with different diamond concentrations (4, 6, 8, 10 g/dm³). This study presents the surface morphology and structure of the produced coatings. The surface roughness, coating thickness (XRF), mechanical properties (DSI), and adhesion of coatings to substrates (scratch tests) were also characterized. The coatings were also tested to assess their solderability, including their spreadability, wettability of the solder, durability of solder-coating bonds, and a microstructure study. [ABSTRACT FROM AUTHOR]

Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)