Determination of Photothermal and EMI Shielding Efficiency of Graphene–Silver Nanoparticle Composites Prepared under Low-Dose Gamma Irradiation.

Silver nanoparticles (Ag NPs) have been produced by low-dose (1–20 kGy) gamma irradiation of silver nitrate in the presence of graphene-based material (graphene oxide or electrochemically exfoliated graphene). The large surface area of those graphene-based materials combined with the presence of oxygen-containing functional groups on the surface provided successful nucleation and growth of Ag nanoparticles, which resulted in a uniformly covered graphene surface. The obtained Ag nanoparticles were spherical with a predominant size distribution of 10–50 nm for graphene oxide and 10–100 nm for electrochemically exfoliated graphene. The photothermal efficiency measurement showed a temperature increase upon exposure to a 532 nm laser for all samples and the highest photothermal efficiency was measured for the graphene oxide/Ag NP sample prepared at 5 kGy. Electromagnetic interference (EMI) shielding efficiency measurements showed poor shielding for the composites prepared with graphene oxide. On the other hand, all composites prepared with electrochemically exfoliated graphene showed EMI shielding to some extent, and the best performance was measured for the samples prepared at 5 and 20 kGy doses. [ABSTRACT FROM AUTHOR]

Copyright of Nanomaterials (2079-4991) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)