Fire Risk of Polyethylene (PE)-Based Foam Blocks Used as Interior Building Materials and Fire Suppression through a Simple Surface Coating: Analysis of Vulnerability, Propagation, and Flame Retardancy.

Building fires can spread through surface combustion of both combustible and interior finishing materials. Recently, the use of foam blocks as interior materials for high-rise residential buildings has increased. However, as foam blocks are primarily composed of polyethylene, they are not flame-retardant and can readily burn and the fire can spread, leading to large-scale damage. Herein, the fire hazard and diffusion characteristics of foam blocks were compared with those of flame-retardant and general wallpapers to confirm the risk of fire. The fire risk of the foam blocks was confirmed using flammability, cone calorimetry, and spread-of-flame analyses. Based on a comparative analysis of the fire risk of foam blocks, the average total heat release was 11.2 MJ/m. This is approximately three times higher than the average heat release rate of the flame-retardant wallpaper and approximately two times higher than that of the general wallpaper. The foam blocks ignited rapidly owing to fire and generated large amounts of combustion gas and heat. To prevent such a fire, 5 wt% montmorillonite (MMT) was simply coated after surface modification to suppress the occurrence of fire. Various flame-retardant materials, surface modifications, and fire safety systems must be developed to prevent fire hazards. [ABSTRACT FROM AUTHOR]

Copyright of Fire (2571-6255) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)