Bio-Based Polyurethane Foams from Kraft Lignin with Improved Fire Resistance.

Rigid polyurethane foams (RPUFs) were synthesized using exclusively lignin-based polyol (LBP) obtained via the oxyalkylation of kraft lignin with propylene carbonate (PC). Using the design of experiments methodology combined with statistical analysis, the formulations were optimized to obtain a bio-based RPUF with low thermal conductivity and low apparent density to be used as a lightweight insulating material. The thermo-mechanical properties of the ensuing foams were compared with those of a commercial RPUF and a RPUF (RPUF-conv) produced using a conventional polyol. The bio-based RPUF obtained using the optimized formulation exhibited low thermal conductivity (0.0289 W/m·K), low density (33.2 kg/m³), and reasonable cell morphology. Although the bio-based RPUF has slightly lower thermo-oxidative stability and mechanical properties than RPUF-conv, it is still suitable for thermal insulation applications. In addition, the fire resistance of this bio-based foam has been improved, with its average heat release rate (HRR) reduced by 18.5% and its burn time extended by 25% compared to RPUF-conv. Overall, this bio-based RPUF has shown potential to replace petroleum-based RPUF as an insulating material. This is the first report regarding the use of 100% unpurified LBP obtained via the oxyalkylation of LignoBoost kraft lignin in the production of RPUFs. [ABSTRACT FROM AUTHOR]

Copyright of Polymers (20734360) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)