Thermal Characterization of Kraft Lignin Prepared from Mixed Hardwoods.

Thermal characterization of kraft lignin (KL) prepared from mixed hardwoods was conducted to determine their thermal and thermooxidative stability, glass transition temperature (Tg), pyrolysis products composition, and syringyl/guaiacyl ratio. Two milled wood lignins (MWLs) from acacia (MWL-aca) and mixed hardwoods (MWL-mhw), the same hardwood species employed in the production of KL, were also characterized for comparison with KL. Thermogravimetric analysis (TGA) indicated that KL had higher thermal and thermo-oxidative stability than MWLs. Based on differential scanning calorimetry (DSC), the Tg of KL was 63.2 °C, while MWLs gave similar values near 165 °C. The syringyl (S), guaiacyl (G), p-hydroxyphenyl (H) composition of KL acquired from pyrolysis-gas chromatography/mass spectrometry (Py-GC/MS) at 675 °C was 48:44:8 (S/G ratio 1.07), while MWL-aca and MWL-mhw were 31:60:9 and 46:48:6, respectively. [ABSTRACT FROM AUTHOR]