INFLUENCE OF DUAL FILLER REINFORCEMENT ON THE CURING AND TRIBO-MECHANICAL BEHAVIOUR OF NATURAL RUBBER NANOCOMPOSITE FOR TIRE TREAD APPLICATION.
Item request has been placed!
×
Item request cannot be made.
×
![loading](/sites/all/modules/hf_eds/images/loading.gif)
Processing Request
- معلومة اضافية
- نبذة مختصرة :
A huge amount of carbon black (40-60 phr) was commonly used as a reinforcing material in manufacturing of tires to improve the technical properties of pure rubber. Carbon black causes severe health hazard like skin cancer, respiratory problem due to its fly loss property. This study focusses on reducing the usage of carbon black by replacing it with minimal quantity of nanoclay to compensate the technical properties of rubber. Natural Rubber nanocomposite are fabricated using solution and mechanical mixing method in presence and absence of compatibilizer. Cure characteristics, wear test and mechanical properties were examined. NR nanocomposite with dual filler in presence of compatibilizer showed enhancement in torque values, mechanical and wear resistant property. Wear resistance, tensile strength and modulus of dual filler nanocomposite was increased by 66.7%, 91% and 85% when compared to pure NR. Hence NR nanocomposite with dual filler in presence of compatibilizer was found as a proving and possible nanocomposite for tire application. [ABSTRACT FROM AUTHOR]
- نبذة مختصرة :
Copyright of Archives of Metallurgy & Materials is the property of Polish Academy of Sciences and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
No Comments.