Shape regulation of high-index facet nanoparticles by dealloying.

NANOPARTICLES; PLATINUM; ANTIMONY; SILICON wafers; CURRENT density (Electromagnetism); ELECTROLYTIC oxidation; FORMIC acid

Tetrahexahedral particles (~10 to ~500 nanometers) composed of platinum (Pt), palladium, rhodium, nickel, and cobalt, as well as a library of bimetallic compositions, were synthesized on silicon wafers and on catalytic supports by a ligand-free, solid-state reaction that used trace elements [antimony (Sb), bismuth (Bi), lead, or tellurium] to stabilize high-index facets. Both simulation and experiment confirmed that this method stabilized the {210} planes. A study of the PtSb system showed that the tetrahexahedron shape resulted from the evaporative removal of Sb from the initial alloy—a shape-regulating process fundamentally different from solution-phase, ligand-dependent processes. The current density at a fixed potential for the electro-oxidation of formic acid with a commercial Pt/carbon catalyst increased by a factor of 20 after transformation with Bi into tetrahexahedral particles. [ABSTRACT FROM AUTHOR]

Copyright of Science is the property of American Association for the Advancement of Science and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)