EFFECT OF Y2O3 NANOPARTICLES ON CORROSION STUDY OF SPARK PLASMA SINTERED DUPLEX AND FERRITIC STAINLESS STEEL SAMPLES BY LINEAR SWEEP VOLTAMMETRIC METHOD.

The microstructure and corrosion properties of spark plasma sintered yttria dispersed and yttria free duplex and ferritic stainless samples were studied. Spark plasma sintering (SPS) was carried out at 1000°C by applying 50 MPa pressure with holding time of 5 minutes. Linear sweep voltammetry (LSV) tests were employed to evaluate pitting corrosion resistance of the samples. Corrosion studies were carried out in 0.5, 1 and 2 M concentration of NaCl and H2SO4 solutions at different quiet time of 2, 4, 6, 8 and 10 seconds. Yttria dispersed stainless steel samples show more resistance to corrosion than yttria free stainless steel samples. Pitting potential decreases with increase in reaction time from 2 to 10 seconds. Similarly, as concentration of NaCl and H2SO4 increases from 0.5 M to 2 M the corrosion resistance decrements due to the availability of more Cl^¯ and SO4 ^2¯ ions at higher concentration. [ABSTRACT FROM AUTHOR]

Copyright of Archives of Metallurgy & Materials is the property of Polish Academy of Sciences and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)