A Combinatorial Study of Photoelectrochemical Properties of Fe-W-O Thin Films.

A continuous mixed Fe-W-O thin-films materials library was fabricated by means of reactive co-sputtering from elemental iron and tungsten targets in argon/oxygen. The materials library was screened for its local photoelectrochemical properties by using an automated optical scanning droplet cell. Local scanning electron microscopy (SEM) and electron-dispersive Xray spectroscopy (EDX) measurements of the materials library were performed to correlate the composition, morphology, and photocurrents. The iron content was varied in the range from Fe32W68Ox to Fe81W19Ox. A strong dependence of the film morphology and the measured photocurrents on the composition was observed with a maximal photocurrent from a measurement area containing 55 at% iron. The most photoactive area showed a porous structure with a high surface area. The bandgap values of these materials were assessed by photocurrent spectroscopy and showed a systematic variation of the bandgap values with the composition. [ABSTRACT FROM AUTHOR]

Copyright of ChemPlusChem is the property of Wiley-Blackwell and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)